PENGARUH PENAMBAHAN SILIKON TERHADAP KEKERASAN DAN KEKUATAN TARIK DAUR ULANG ALUMUNIUM LIMBAH RUMAH TANGGA DENGAN PENGECORAN SENTRIFUGAL

Megananda, Ribut (2024) PENGARUH PENAMBAHAN SILIKON TERHADAP KEKERASAN DAN KEKUATAN TARIK DAUR ULANG ALUMUNIUM LIMBAH RUMAH TANGGA DENGAN PENGECORAN SENTRIFUGAL. Skripsi (S1) thesis, Universitas Muhammadiyah Ponorogo.

	Text (SURAT PERSETUJUAN UNGGAH KARYA ILMIAH) 1. SURAT PERSETUJUAN UNGGAH KARYA ILMIAH .pdf Download (481kB)
	Text (HALAMAN DEPAN) 2. HALAMAN DEPAN.pdf Download (1MB)
	Text (BAB I) 3. BAB I.pdf Download (436kB)
	Text (BAB II) 4. BAB II.pdf Restricted to Repository staff only Download (1MB)
	Text (BAB III) 5. BAB III.pdf Restricted to Repository staff only Download (657kB)
	Text (BAB IV) 6. BAB IV.pdf Restricted to Repository staff only Download (1MB)
	Text (BAB V) 7. BAB V.pdf Restricted to Repository staff only Download (241kB)
	Text (DAFTAR PUSTAKA) 8. DAFTAR PUSTAKA.pdf Download (416kB)
	Text (LAMPIRAN) 9. LAMPIRAN.pdf Restricted to Repository staff only Download (796kB)
	Text (SKRIPSI FULL TEXT) 10. SKRIPSI FULL TEXT.pdf Restricted to Repository staff only Download (3MB)

Abstract

ABSTRAK
Penggunaan aluminium di dunia semakin meningkat, dan sifat-sifat aluminium terus ditingkatkan. Unsur lainnya adalah paduan aluminium dan silikon (AI-Si), yang mempunyai sifat mekanikal, tahan terhadap korosi yang sangat baik dan kemampuan las. Penelitian ini bertujuan untuk mengetahui bagaimana hasil uji kekerasan dan uji tarik alumunium (Al) dengan penambahan unsur silikon (Si) 6%, 8&, dan 10%. Pada uji kekerasan ini menggunakan uji kekerasan brinell dimana uji lekukan sederhana untuk mengukur nilai kekerasan berbagai material. Sedangkan uji tarik menggunakan uji untuk mengetahui nlai tegangan maupun regangan pada spesimen. Pengecoran sentrifugal dilakukan pada penelitian ini karena metode ini mempunyai keunggulan mampu menghasilkan coran berbentuk silinder dengan produktivitas tinggi dan kualitas coran tinggi. Hasil dari penelitian ini adalah pada uji kekerasan dengan variasi silikon 6% yaitu 27,62 BHN. Namun hasil turun 26,68 BHN dengan variasi silicon 8% dan pada variasi silicon 10% naik menjadi 30,54 BHN. Jadi semakin besar nilai penambahan unsur silikon pada alumunium limbah rumah tangga semakin besar juga nilai kekerasanya tetapi semua itu memiliki batas persentase yang tepat untuk menambah kekerasannya juga. Hal itu disebabkan juga karena temperature tuang dan adanya kerak maupun kotoran pada spesimen. Hasil pada uji tarik penambahan unsur silikon 6% hasil yang diperoleh sebesar 73,5 MPa, mengalami kenaikan pada unsur silikon 8% sebesar 79,4 MPa dan meningkat lagi sebesar 94,5 MPa dengan penambahan unsur silikon 10%. Dapat dijelaskan bahwa semakin tinggi penambahan unsur silikon pada alumunium limbah rumah tangga semakin tinggi pula kekuatan tarik yang didapatkan.
Kata Kunci: Alumunium, Uji Kekerasan, Uji Tarik
ABSTRACT
The use of aluminum in the world is increasing, and the properties of aluminum are constantly being improved. Another element is an alloy of aluminum and silicon (AI-Si), which has excellent mechanical properties, corrosion resistance and weldability. This research aims to determine the results of the hardness test and tensile test of aluminum (Al) with the addition of 6%, 8&, and 10% silicon (Si). This hardness test uses the Brinell hardness test, which is a simple indentation test to measure the hardness value of various materials. Meanwhile, the tensile test uses a test to determine the stress and strain values in the specimen. Centrifugal casting was carried out in this research because this method has the advantage of being able to produce cylindrical castings with high productivity and high casting quality. The results of this research were the hardness test with a 6% silicon variation, namely 27.62 BHN. However, the yield decreased by 26.68 BHN with an 8% silicon variation and with a 10% silicon variation it increased to 30.54 BHN. So the greater the value of adding silicon elements to household waste aluminum, the greater the hardness value, but all of this has an appropriate percentage limit to increase the hardness too. This is also caused by the pouring temperature and the presence of crust or dirt on the specimen. The results of the tensile test with the addition of 6% silicon element were 73.5 MPa, there was an increase for 8% silicon element of 79.4 MPa and another increase of 94.5 MPa with the addition of 10% silicon element. It can be explained that the higher the addition of silicon elements to household waste aluminum, the higher the tensile strength obtained..
Keywords: Aluminum, Hardness Test, Tensile Test

Item Type:	Thesis (Skripsi (S1))
Uncontrolled Keywords:	Alumunium, Uji Kekerasan, Uji Tarik
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Faculty of Engineering
Depositing User:	ft . userft
Date Deposited:	06 Sep 2024 01:46
Last Modified:	21 May 2025 07:12
URI:	https://eprints.umpo.ac.id/id/eprint/14993

Actions (login required)

View Item